Expanded Graphite packing with corrosion inhibitor, reinforced with INCONEL wire.
Very flexible packing and good alternative to pre-formed pure graphite rings, STYLE-902 I combines the benefits of a coil-form packing with the sealing efficiency of pre¬formed pure graphite rings; high pressure and extrusion resistance; excellent thermal conductivity; suitable for a wide temperature range and can be sealed under ideal mechanical conditions of lower temperature.
Application Areas: It can handle most chemicals, acids & alkalis. Excellent use in Steam turbines, high temperature motor-actuated valves and for high temperature and high pressure valve applications in general.
Application Media: Steam Water, Fuel Gases, chemicals, mineral and synthetic oils, effluents, suitable in all processes except with highly oxidizing media.
Benefits: STYLE- 902 I is suitable for a wide range of applications and can reduce stock inventories considerably. Very economic alternatives to asbestos packings. Easy to install and reduce maintenance time.
|
|
Ratating
|
Reciprocating
|
Static
|
|---|---|---|---|
|
Pressure
|
|
|
|
|
1.1 g/cm3
|
|
|
|
|
-240 +450 Deg.0 Steam+650 Inert Gas-1000
|
|
|
|
|
0~14
|
|
|
The KWO Quality Management is certified according to DIN EN ISO 9001. Our suppliers are also integrated in this quality system. We use exclusively high quality raw materials in the fabrication of our products, which provide the highest level of safety and reliability.
Width* | Thickness [mm] | |||
2 | 3 | 6 | 9 | |
10 | X | X | X | |
15 | X | X | X | X |
20 | X | X | X | X |
25 | X | X | X | X |
30 | X | X | X | X |
40 | X | X | X | X |
50 | X | X | X | |
55 | X | X | X | |
60 | X | X | X | |
The p-T diagram indicates the service limits considering the simultaneous influence of pressure and temperature.
Range 1: Typical service limits
Range 2: Maximum application limits, after technical verification
| QMIN (0,01) | 28 Mpa | DIN EN 13555 |
| QS MIN (0,01) | <<10 Mpa | DIN EN 13555 |
| PQR (at Qsmax 20°C) | 0,95 | DIN EN 13555 |
| PQR (at Qsmax 150°C) | 0,64 | DIN EN 13555 |